Tungsten carbide Balls

Tungsten carbide Balls

  • Tungsten Carbide Ball
  • Tungsten Carbide Ball
  • Tungsten Carbide Ball
  • Tungsten Carbide Ball
  • Tungsten Carbide Ball
  • Tungsten Carbide Ball
Tungsten Carbide BallTungsten Carbide BallTungsten Carbide BallTungsten Carbide BallTungsten Carbide BallTungsten Carbide Ball

Tungsten Carbide Ball

Tungsten carbide balls and valve seats have the compositions of tungsten carbide(WC) and Co or Ni or Mo additives. With high compression strength, excellent wear resistance and well shock and impact resistance, tungsten carbide balls and valve seats are widely supplied as ballrolling element in bearing industry, pump valve spool for fluid seal, check valve for petroleum digger, industrial sprayers to regulate the flow of fertilizers or pesticides to crops. 

Tungsten carbide balls can be also applied in a drastically different application, it can be employed as pen balls due to their inert chemical properties.  Besides, in miniature flow control devices, such as medical instrumentation and inkjet printing, tungsten carbide balls are also frequently used.



General Specification

 

Grade

Allowable Ball Diameter Variation

Deviation from Spherical Form

Surface Roughness Arithmetical Average

Basic Diameter Tolerance

Allowable Lot Diameter Variation

3

0.0762μm  (0.000003")

0.0762μm    (0.000003")

0.0127μm   (0.0000005")

±0.762μm            (±0.00003")

0.0127μm   (0.000005")

5

0.127μm      (0.000005")

0.127μm    (0.000005")

0.02μm         (0.0000008")

±1.27μm              (±0.00005")

0.254μm            (0.00001")

10

0.254μm         (0.00001")

0.254μm         (0.00001")

0.0254μm    (0.000001")

±2.54μm              (±0.0001")

0.508μm     (0.00002")

15

0.381μm            (0.000015")

0.381μm            (0.000015")

0.0254μm    (0.000001")

±2.54μm              (±0.0001")

0.762μm              (0.00003")

16

0.4064μm             (0.000016")

0.4064μm             (0.000016")

0.0254μm    (0.000001")

±2.54μm              (±0.0001")

0.8128μm             (0.000032")

24

0.6096μm                  (0.000024")

0.6096μm                  (0.000024")

0.0508μm     (0.000002")

±2.54μm              (±0.0001")

1.2192μm          (0.000048")

25

0.635μm   (0.000025")

0.635μm   (0.000025")

0.0508μm     (0.000002")

±2.54μm              (±0.0001")

1.27μm          (0.00005")

48

1.2192μm          (0.000048")

1.2192μm          (0.000048")

0.0762μm      (0.000003")

±5.08μm              (±0.0002")

2.4384μm     (0.000096")

50

1.27μm         (0.00005")

1.27μm         (0.00005")

0.0762μm      (0.000003")

±7.62μm             (±0.0003")

2.54μm             (0.0001")

100

2.54μm            (0.0001")

2.54μm            (0.0001")

0.127μm               (0.000005")

±12.7μm                (±0.0005")

5.08μm           (0.0002")

200

5.08μm     (0.0002")

5.08μm     (0.0002")

0.2032μm                    (0.000008")

±25.4μm                 (±0.001")

10.16μm                        (0.0004")

300

7.62μm          (0.0003")

7.62μm          (0.0003")

 _

±25.4μm                     (±0.001")

15.24μm                 (0.0006")

500

12.7μm                (0.0005")

12.7μm                (0.0005")

 _

±50.8μm                (±0.002")

25.4μm               (0.001")

1000

25.4μm                 (0.001")

25.4μm                 (0.001")

 _

±127.0μm             (±0.005")

50.8μm             (0.002")

2000

50.8μm            (0.002")

50.8μm            (0.002")

 _

±127.0μm             (±0.005")

101.6μm           (0.004")

3000

76.2μm              (0.003")

76.2μm              (0.003")

 _

±127.0μm             (±0.005")

152.4μm    (0.006")


ASTM B 777-99

 

Class

_

1

2

3

4

Tungsten Nominal %

_

90

92.5

95

97

Density (g/cc)

_

16.85-17.25

17.15-17.85

17.75-18.35

18.25-18.85

Hardness (HRC) Max

_

32

33

34

35

Ultimate Tensile Strength

ksi

110

110

105

100

 _

Mpa

758

758

724

689

Yield Strength at 0.2% off-set

ksi

75

75

75

75

 _

Mpa

517

517

517

517

Elongation, %


5

5

3

2

AMS-T-21014

 

    _

Class 1

Class 1

Class 2

Class 2

Composition

90W7Ni3Fe

91W6Ni3Fe

92W5Ni3Fe

93W4Ni3Fe

Density (g/cm3)

17.1±0.15

17.25±0.15

17.50±0.15

17.60±0.15

Heat Treatment

Sintering

Sintering

Sintering

Sintering

Tensile Strength (MPa)

900-1000

900-1000

900-1100

900-1100

Elongation (%)

18-29

17-27

16-26

16-24

Hardness(HRC)

24-28

25-29

25-29

26-30

AMS-T-21014

Class 3

Class 3

Class 4

 _

Composition

95W3Ni2Fe

96W3Ni1Fe

97W2Ni1Fe

 _

Density (g/cm3)

18.10±0.15

18.30±0.15

18.50±0.15

 _

Heat Treatment

Sintering

Sintering

Sintering

 _

Tensile Strength (MPa)

920-1100

920-1100

920-1100

 _

Elongation (%)

42665

42602

42534

 _

Hardness(HRC)

27-32

28-34

28-36

 _

 



Zhuzhou Newmetal Materials Co., Ltd.

ADDRESS7th Floor, Zhishang Hitech Building, No.9 Zhongda Road, Zhuzhou city, Hunan

Tel:+86-731-28622059,Fax:0731-28622159
Email:sales@nmtmetals.com

Skype:aliceshen0314

Whatsapp/Wechat:+86-15116075317



Drop Us a Line